Single-chamber high-pressure High temperature vacuum gas quenching furnace
Gas Pressure Cooling
Gas pressure can be increased up to 0.5 MPa·G during cooling. This allows for easy quenching of large pieces of die steel and high-speed steel.
Distortion-Free
During cooling, cooling gas is sprayed into the furnace chamber from above and below to provide uniform cooling. This results in extremely low levels of distortion.
Applications
Heat Treatment of Metals
Vacuum Quenching
Vacuum Tempering
Vacuum Annealing
Precipitation Treatment
Solution Treatment
Application
Quenching of high speed steel, tool and die steel, stainless steel.
Solid solution treatment of stainless steel and titanium alloys.
Magnetic materials Vacuum heat treatment of magnetic materials.
High temperature brazing and vacuum sintering.
Performance features
Convection heating, to achieve rapid and uniform heating of low-temperature strands.
The heating chamber structure in the furnace provides more uniform heating, less power loss and energy saving.
Using a new type of carbon felt composite material, it is resistant to high temperature and high pressure airflow erosion, and the heat shield has a longer service life and is easier to maintain.
High-speed and high-pressure fans and high-efficiency copper-copper heat exchangers achieve rapid cooling.
Alternate cooling method achieves uniform cooling and ensures minimal deformation of the workpiece.
The cooling pressure and wind speed of the locomotive are adjustable to achieve graded cooling.
The vertical furnace adopts screw drive, which is flexible, safe and reliable.
Optional graphite or all-metal heating chamber.
Optional fully intelligent industrial computer control and a manual operating system are available, which are easy to learn, understand and operate.
Specification
| Name | Vacuum Gas Quenching Furnace |
| Air Cooling Pressure | 2/4/6/10/15/20bar |
| Chamber Size | 400*300*300mm (Custom Made) |
| Core Components | Plc, Engine, Bearing, Gearbox, Motor, Pressure Vessel, Gear, Pump |
| Dimension(L*W*H) | 300*300*500-1000*1000*2000(Customized) |
| Heater | Mosi2 Heating,Mo Belt, Tungsten, Graphite, Simo, Sic |
| Loading Capacity | 50-1500kg |
| Power (Kw) | 36-500kw |
| Pressure Increasing Rate | 0.65/0.67/0.68pa/H |
| Structure | Horizontal, Vertical, Batch, Continuous |
| Ultimate Vacuum | 3.0*10-4 Pa |
| Voltage | Optional Customized(220v/380v/660v) |
| Working Temperature | 0-1650 Degrees |
| Weight | 2t-35t |
| Amosphere Protect | Gas Protection |
| Furnace Structure | Double Shell With Water Cooling |
| Furnace Temperature Uniformity | ±5 .C |
| Usage | Lab Sintering/Brazing/Quenching/Heating Treatment /Bright Annealing For Steels |
| Key Selling Points | Easy To Operate/High Productivity/Multifunctional/Energy Saving |
| Melting Material | Metal Workpiece |
|
Valid zone
|
Maximum temperature (℃)
|
Heating power (kw)
|
Ultimate vacuum (Pa)
|
Gas cooling pressure (bar)
|
|
450x300x300
|
1320
|
40
|
5x10-3or4x10-1
|
10
|
|
600x400x400
|
1320
|
80
|
5x10-3or4x10-1
|
10
|
|
700x500x500
|
1320
|
120
|
5x10-3or4x10-1
|
10
|
|
900x600x600
|
1320
|
150
|
5x10-3or4x10-1
|
10
|
|
1500x800x800
|
1320
|
300
|
5x10-3or4x10-1
|
10
|